Study of Creep Cavitation in Welded Creep Crack Growth Test Specimens
Strain-relief cracking is a generic creep failure mode that has been observed in many welded stainless steel structures operating at high temperatures in UK nuclear power plant.... -
Intergranular stress generation during high temperature creep-fatigue loading
Intergranular stresses, generated during cyclic loading of AISI type 316H stainless steel can significantly affect the creep deformation of this material. However,... -
In-situ assessment of stress build-up during thermal cycling of the diffusion...
Direct bonded copper(DBC)substrate,the most commonly used substrate in the power modules of electric vehicles for the thermal management,has reliability issues in high...