The dataset contains supplemental materials for Fluoropolymer Coatings for Solar Cover Glass: Anti-Soiling Mechanisms in the Presence of Dew.
Table of Contents
Fig. S1. Soiling rate using CDA (cloud deposition apparatus) measured by a decrease in %T at λ=550nm as a function of dust exposure time (open-door time).
Fig. S2. Initial Direct Light Percent Transmittance (%T)
Fig. S3. Atomic Force Microscopy (AFM) Images of Test Surfaces
Fig. S4. Atomic Force Microscopy (AFM) Images of Test Surfaces
Fig. S5. Soiling plots of all individual samples: Percent Transmittance at 550 nm
Fig. S6. Soiling plots of all individual samples: Percent Surface Area Covered by Dust
Fig. S7 Large Area View of Hydrophobic Coated Glass After One Dew-Dust-Dry Cycle
Fig. S8. Effect of Soiling Sequence: Dust Deposited on Condensate vs Condensation onto a Dust-coated Surface.
Fig. S9. No-Touch Cleaning after Dry Soiling
Fig. S10. Photographs of Bare Glass and Hydrophobic Surfaces after soiling (before controlled cleaning) and after controlled cleaning
Table S1. Contact Angle Hysteresis and Sliding Angles of the Test Substrates
Table S2. Supplementary Videos